Application: | Food, Household, Apparel |
---|---|
Feature: | Moisture Proof, Bio-Degradable, Disposable |
Material: | PLA Pbat |
Shape: | Plastic Bags |
Making Process: | Composite Packaging Bag |
Raw Materials: | PLA Pbat |
Suppliers with verified business licenses
Product Paramenters | |
Brand Name | YUANXIAN POLYMER |
Product Name | Shopping Bags and Film |
Material | PLA+PBAT |
Color | Customized |
Size(CM) | Customized |
Features | -Fully biodegradable, more environmentally friendly -Good load-bearing, no stranglehold -It is tightly sealed and not easy to leak -Strong handle, stretch performance is good. -Constant temperature process and tight edge sealing -Excellent ink, clear printing |
Application | T-shirt bags, these are generally used to carry purchases in grocery market, retail stores,restaurants,convenience stores,super market. |
Our Advantage | 1. Professional ODM&OEM experience. |
2. Professional equipment produces high quality products. | |
3. Customer success plan. | |
4. Experience Focusing on the R&D of plastic products. | |
5. Fast delivery time. | |
6. 100% safe payment. |
Size:
- Bag Size, Bag Qty per package and package ways could be customized.Size | Dimension, cm | Thickness, mic |
Small | 35x(20+7x2) | 20 |
Medium | 50x(35+7x2) | 25 |
Large | 60x(40+7x2) | 25 |
Modified Material
Film Blowing Grade YPMH-S200
Film Blowing Grade PLA Modified Material
PLA+PBAT+STARCH
Item Code: YPMH-S200
Recommended application
Shopping vest bag, wrist bag, roll bag, food preservation bag; Electronic product packaging film, household
Appliance packaging film, medical hygiene film, etc.
Product characteristics
1) Good coloring performance, stable melt strength, and can be directly processed into various films;
2) It is usually light white or light yellow, has fragrance, is easy to be decomposed by microorganisms, and has natural antistatic property;
3) Good heat stability of raw materials, good recyclability of leftover materials, high temparature and strong shear force;
4) This product has low moisture content. It is vacuum packed and can be used after opening.
Material properties
Item | Test method | Conditions for item | Unit | Result[1] |
Melt flow rate | 1S0 1133 | 190ºC, 2.16kg | g/10min | 4.0-7.0 |
Density | 1S0 1183 | 23ºC | g/cm3 | 1.27-1.32 |
Melting point | DSC | - | ºC | 110-130 |
Temperature | Typical value[2] | Reference range | |
Melting temperature | 120ºC | 115-125ºC | |
Temperature of film blowing heating area | Posterior segment | 025ºC | 120-130ºC |
Middle segment | 130ºC | 125-135ºC | |
Anterior segment | 135ºC | 130-140ºC | |
Mould head temperature | 135ºC | 130-140ºC | |
Upper limit of processing temperature | 180ºC |
Characteristics[4] | Test method | Conditions for testing | Unit | Typical values[5] |
Tensile strength longitudinal/transverse | 1S0 527 | 25ºC | MPa | 21/12 |
Elongation at break longitudinal/transverse | 1S0 527 | 25ºC | % | 250/600 |
Dart impact | 1S0 7765-1 | 25ºC | g |
150 |
Item | Test method | Conditions for item | Unit | Result[1] |
Melt flow rate | 1S0 1133 | 190ºC, 2.16kg | g/10min | 3.0-6.0 |
Density | 1S0 1183 | 23ºC | g/cm3 | 1.38-1.43 |
Melting point | DSC | - | ºC | 110-130 |
Temperature | Typical value[2] | Reference range | |
Melting temperature | 125ºC | 120-130ºC | |
Temperature of film blowing heating area | Posterior segment | 145ºC | 140-150ºC |
Middle segment | 145ºC | 140-150ºC | |
Anterior segment | 150ºC | 140-150ºC | |
Mould head temperature | 150ºC | 140-150ºC | |
Upper limit of processing temperature | 190ºC |
Characteristics[4] | Test method | Conditions for testing | Unit | Typical value[5] |
Tensile strength longitudinal/transverse | 1S0 527 | 25ºC | MPa | 17/13 |
Elongation at break longitudinal/transverse | 1S0 527 | 25ºC | % | 300/500 |
Dart impact | 1S0 7765-1 | 25ºC | g | 190 |
[3]Typical films are produced by film blowing mechanism with the material YPMH-M300, film thickness is 28 microns;
[4]The data are measured by the newly produced film and can not be used as the basis for judging material quality;
[5]The above data are typical values, not guaranteed values
1. Q: What's your main material?
Our main materials are PLA,PBS,PBAT and Corn Starch. The materials are 100% Compostable and Biodegradable, they can be degraded into H20 and C20 completely.Suppliers with verified business licenses