| Application: | Food, Household, Apparel |
|---|---|
| Feature: | Moisture Proof, Bio-Degradable, Disposable |
| Material: | PLA PBAT |
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Product Parameters | |
| Brand Name | YUANXIAN POLYMER |
| Product Name | Zipper Locking Bag / Ziplock Bag |
| Material | PLA/PBAT |
| Color | Customized |
| Size(CM) | Customized |
| Features | - 100% biodegradable & compostable - Point Breaking design - Service life: 10 months - Printing :1 color on one side - Size: can be customized |
| Application | Supermarket / Household storage bag Food / Fruit / Vegetables fresh food bag Freezer Food |
| Our Advantage | 1. Professional ODM&OEM experience. 2. Professional equipment produces high quality products. 3. Customer success plan. 4. Experience Focusing on the R&D of plastic products. 5. Fast delivery time. 6. 100% safe payment. |
| ziplock bag | L x W(cm) | Thickness(mic) |
| 18*17 | 50 | |
| 22*15 | 50 |
The Lactic acid (PLA) monomer is made from fermented plant starch such as from corn.
Polylactic acid (PLA) can be completely decomposed into carbon dioxide (CO2) and water (H2O) under natural conditions after being discarded.
Item No: YPRX-PLA01
Molecular Formula: H-[OCHCH3CO]n-OH
CAS NO: 26100-51-6
Color: White
Standard: GB/T 29284-2012
| Item | unit | Result |
| Monomer content and D-content | % | ≤0.3 |
| Density | g/cm3 | >1.24 |
| Particle Diameter | mm | 2 |
| Melt index (190ºC/2.16kg) | g/10min | 10 |
| Melt point | ºC | >165 |
| Tensile Strength at Break | MPa | >45 |
| Elongation at break | % | >5 |
| Tensile Modulus | GPa | 6.5 |
| Notch Impact Strength | kJ/m2 | >4 |
| HDT(0.45Mpa) | ºC | >100 |
| Bending strength | Mpa | >70 |
| Transmittance | % | >95 |
Degradation Rate |
% | >95 |
| Item | Unit | PP | GPP | PET | PLA |
| Density | g/cm3 | 0.9-0.91 | 1.04-1.09 | 1.3-1.4 | 1.25 |
| Melt Index | g/10min | 0.2-20 | 1.5-30 | -- | 1-30 |
| Tensile strength | MPa | 29.6-35 | ≥58.8 | ≥60 | ≥50 |
| Elongation | % | 200-700 | 1.0-2.5 | 30-70 | ≥5 |
| Transmittance | % | 85-88 | 88-92 | 90-92 | 90-95 |
| No | Item | Unit | YPRX-PBS01 | YPRX-PBS02 | ||
| 1 | Density, 25ºC | Standard value | g/cm3 | 1.25 | ||
| Deviation | +0.03 | |||||
| 2 | Density, 25ºC | ºC | 105-116 | |||
| 3 | MFR | Standard value | g/10min | ≤10 | 10-20 | |
| Deviation | ||||||
| 4 | Moisture | % | ≤0.2 | |||
| 5 | Hydroxyl content | mol/t | ≤50 | |||
| 6 | Color value | L value | Standard value | -- | ≥75 | |
| A value | Nominal value | -- | ≤5 | |||
| Deviation | +0.5 | |||||
| B value | Nominal value | -- | ≤11 | |||
| Deviation | +1 | |||||
| 7 | Breaking tensile strength | Mpa | ≥25.0 | |||
| 8 | Tensile strain at breaking | % | ≥150 | |||
| 9 | Bending strength | Mpa | ≥25.0 | |||
| 10 | Bending modulus | Mpa | ≥400 | |||
| No | Item | Unit | Value | ||
| 1 | Density, 25ºC | g/cm3 | 1.23+0.03 | ||
| 2 | Melting Point, pm | ºC | 110-145 | ||
| 3 | MFR | g/10min | 2.5-4.5 | ||
| 4 | Moisture | % | ≤0.1 | ||
| 5 | Hydroxyl content | mol/t | ≤50 | ||
| 6 | Color value | L value | Standard value | -- | ≥70 |
| A value | Nominal value | -- | ≤5 | ||
| Deviation | +1 | ||||
| B value | Nominal value | -- | ≤10 | ||
| Deviation | +1 | ||||
| 7 | Breaking tensile strength | Mpa | ≥15 | ||
| 8 | Tensile strain at breaking | % | ≥500 | ||
| 9 | Bending strength | Mpa | ≥3 | ||
| 10 | Bending modulus | Mpa | ≥30 | ||
| 11 | Vicat softening point A50 | ºC | ≥80 | ||
| 12 | Ash content | % | ≤0.1 | ||
Modified Material
Film Blowing Grade YPMH-S200
Film Blowing Grade PLA Modified Material
PLA+PBAT+STARCH
Item Code: YPMH-S200
Recommended application
Shopping vest bag, wrist bag, roll bag, food preservation bag; Electronic product packaging film, household
Appliance packaging film, medical hygiene film, etc.
Product characteristics
1) Good coloring performance, stable melt strength, and can be directly processed into various films;
2) It is usually light white or light yellow, has fragrance, is easy to be decomposed by microorganisms, and has natural antistatic property;
3) Good heat stability of raw materials, good recyclability of leftover materials, high temparature and strong shear force;
4) This product has low moisture content. It is vacuum packed and can be used after opening.
Material properties
| Item | Test method | Conditions for item | Unit | Result[1] |
| Melt flow rate | 1S0 1133 | 190ºC, 2.16kg | g/10min | 4.0-7.0 |
| Density | 1S0 1183 | 23ºC | g/cm3 | 1.27-1.32 |
| Melting point | DSC | - - |
ºC | 110-130 |
| Temperature | Typical value[2] | Reference range | |
| Melting temperature | 120ºC | 115-125ºC | |
| Temperature of film blowing heating area | Posterior segment | 025ºC | 120-130ºC |
| Middle segment | 130ºC | 125-135ºC | |
| Anterior segment | 135ºC | 130-140ºC | |
| Mould head temperature | 135ºC | 130-140ºC | |
| Upper limit of processing temperature | 180ºC | ||
| Characteristics[4] | Test method | Conditions for testing | Unit | Typical values[5] |
| Tensile strength longitudinal/transverse | 1S0 527 | 25ºC | MPa | 21/12 |
| Elongation at break longitudinal/transverse | 1S0 527 | 25ºC | % | 250/600 |
| Dart impact | 1S0 7765-1 | 25ºC | g |
150 |
[3]Typical film are produced by film blowing mechanism with the material YPMH-M300, film thickness is 28 microns;
[4]The data are measured by the newly produced film and can not be used as the basis for judging material quality;
[5]The above data are typical values, not guaranteed values.
Modified Material
Film Blowing Grade YPMH-M300
Film Blowing Grade PLA Modified Material
PLA+PBAT+STARCH
Item Code: YPMH-M300
Recommended applications
Shopping vest bag, wrist bag, roll bag, food preservation bags; packaging film for electronic products, packaging film for home appliances, medical sanitary films, etc.
Product Features
1) Independent corn tachnology, high product strength, more than 30% higher than the tensile strength of conventional commercial products;
2) Good coloring performance, stable melt strength, and can be directly processed into various films;
3)It is usually light white, fragrant, easy to be decomposed by microorganisms, and has natural antistatic property;
4)The raw materials have good thermostability, good recyclability of leftover materials, and can withstand high temperature and strong shear force.
Material properties
| Item | Test method | Conditions for item | Unit | Result[1] |
| Melt flow rate | 1S0 1133 | 190ºC, 2.16kg | g/10min | 3.0-6.0 |
| Density | 1S0 1183 | 23ºC | g/cm3 | 1.38-1.43 |
| Melting point | DSC | - - |
ºC | 110-130 |
| Temperature | Typical value[2] | Reference range | |
| Melting temperature | 125ºC | 120-130ºC | |
| Temperature of film blowing heating area | Posterior segment | 145ºC | 140-150ºC |
| Middle segment | 145ºC | 140-150ºC | |
| Anterior segment | 150ºC | 140-150ºC | |
| Mould head temperature | 150ºC | 140-150ºC | |
| Upper limit of processing temperature | 190ºC | ||
| Characteristics[4] | Test method | Conditions for testing | Unit | Typical value[5] |
| Tensile strength longitudinal/transverse | 1S0 527 | 25ºC | MPa | 17/13 |
| Elongation at break longitudinal/transverse | 1S0 527 | 25ºC | % | 300/500 |
| Dart impact | 1S0 7765-1 | 25ºC | g |
190 |
[3]Typical films are produced by film blowing mechanism with the material YPMH-M300, film thickness is 28 microns;
[4]The data are measured by the newly produced film and can not be used as the basis for judging material quality;
[5]The above data are typical values, not guaranteed values.
1. Q: What's your main material?
Our main materials are PLA,PBS,PBAT and Corn Starch. The materials are 100% Compostable and Biodegradable, they can be degraded into H20 and C20 completely.
2. Q: What information should I let you know if I want to get a quotation?
The size of the products (Length x Width), if your bag's have the gusset, also please provide the gusset size.
We usually quote you within 24 hours after we get your inquiry. If you are in urgency to get the quotation,please call us or tell us in your mail, so that we could regard your inquiry in priority.
3. Q: The printing: How many colors printing in 1 side or 2 sides?
It will be very useful if you can provide your bag's picture. Of course, samples will be best.
4. Q: What's your MOQ?
Usually 1 tons each kind, the more the cheaper.
5. Q: What is the bag size?
You can measure the length, width and height of the goods that need to packing, we will help you calculate the required size of the bag.
We do customized products, any size & any color we can make according to your requirement.
6. Q: Can you design for me?
According to your requirement, we can add your company logo, website, phone number or your ideas on the bag....
Any color is available. Our profession designer can make design it to for you for free.
Welcome to contact with us for more details!