| Material: | PLA Pbat |
|---|---|
| Feature: | Biodegradable, Compostable, Disposable |
| Application: | Indoor Use, Inside Pet Cage |
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
The Lactic acid (PLA) monomer is made from fermented plant starsh such as from corn.
Polylactic acid (PLA) can be completely decomposed into carbon dioxide (CO2) and water (H2O) under natural conditions after being discarded.
Item No: YPRX-PLA01
Molecular Formula: H-[OCHCH3CO]n-OH
CAS NO: 26100-51-6
Color: White
Standard: GB/T 29284-2012
| Item | Unit | Result |
| Monomer content and D-content | % | ≤0.3 |
| Density | g/cm3 | >1.24 |
| Particle Diameter | mm | 2 |
| Melt index (190ºC/2.16kg) | g/10min | 10 |
| Melt point | ºC | >165 |
| Tensile Strength at Break | MPa | >45 |
| Elongation at break | % | <5 |
| Tensile Modulus | GPa | 3.5 |
| Notch Impact Strength | kJ/m2 | >4 |
| HDT(0.45Mpa) | ºC | >100 |
| Bending strength | Mpa | >70 |
| Transmittance | % | >95 |
| Degradation Rate | % |
>95 |
| Item | Unit | PP | GPP | PET | PLA |
| Density | g/cm3 | 0.9-0.91 | 1.04-1.09 | 1.3-1.4 | 1.25 |
| Melt Index | g/10min | 0.2-20 | 1.5-30 | -- | 1-30 |
| Tensile strength | MPa | 29.6-35 | ≥58.8 | ≥60 | ≥50 |
| Elongation | % | 200-700 | 1.0-2.5 | 30-70 | ≥5 |
| Transmittance | % | 85-88 | 88-92 | 90-92 | 90-95 |
PBS
Polybutylene succinate
Item No: YPRX-PBS01, YPRX-PBS02
Molecular Formula: HO-(CO-(CH2)4-CO-O-(CH2)4-0)n-H
CAS NO: 25777-14-4
Standard: GB/T 30294-2013
Color: Natural white
Raw Material: BDO(1,24-butanediol) Succinic Acid
Application: injection molding tablewares and cutlery textile, fishing net, engineering components medical applications, etc.
PBS is biodegradable and environment-friendly material.
Our PBS has excellent mechanical properties, close to PP and ABS plastics; The heat resistance is good, the thermal deformation temperature is close to 100 centigrade, and the service temperature after modification can exceed 100 centigrade.
PBS is widely used in packaging (including food packaging, cosmetic bottles, drug bottles), tableware, disposable medical supplies, agricultural film, pesticide and fertilizer slow-release materials, biomedical polymer materials and other fields. It can not only meet the demand through petrochemical products, but also produce natural renewable crop products such as cellulose, diary by-products, glucose, fructose and lactose through biological fermentation, so as to realize green circular production from nature and return to nature.
| No | Item | Unit | YPRX-PBS01 | YPRX-PBS02 | ||
| 1 | Density, 25ºC | Standard value | g/cm3 | 1.25 | ||
| Deviation | +0.03 | |||||
| 2 | Density, 25ºC | ºC | 105-116 | |||
| 3 | MFR | Standard value | g/10min | ≤10 | 10-20 | |
| Deviation | ||||||
| 4 | Moisture | % | ≤0.2 | |||
| 5 | Hydroxyl content | mol/t | ≤50 | |||
| 6 | Color value | L value | Standard value | -- | ≥75 | |
| A value | Nominal value | -- | ≤5 | |||
| Deviation | +0.5 | |||||
| B value | Nominal value | -- | ≤11 | |||
| Deviation | +1 | |||||
| 7 | Breaking tensile strength | Mpa | ≥25.0 | |||
| 8 | Tensile strain at breaking | % | ≥150 | |||
| 9 | Bending strength | Mpa | ≥25.0 | |||
| 10 | Bending modulus | Mpa | ≥400 | |||
PBAT (short for polybutylene adipate terephthalate) is a biodegradable random copolyme, specifically a copolyester of adipic acid, 1,4-butanediol and terephthalic acid(from dimethyl terephthalate).
| No | Item | Unit | Value | ||
| 1 | Density, 25ºC | g/cm3 | 1.23+0.03 | ||
| 2 | Melting Point, pm | ºC | 110-145 | ||
| 3 | MFR | g/10min | 2.5-4.5 | ||
| 4 | Moisture | % | ≤0.1 | ||
| 5 | Hydroxyl content | mol/t | ≤50 | ||
| 6 | Color value | L value | Standard value | -- | ≥70 |
| A value | Nominal value | -- | ≤5 | ||
| Deviation | +1 | ||||
| B value | Nominal value | -- | ≤10 | ||
| Deviation | +1 | ||||
| 7 | Breaking tensile strength | Mpa | ≥15 | ||
| 8 | Tensile strain at breaking | % | ≥500 | ||
| 9 | Bending strength | Mpa | ≥3 | ||
| 10 | Bending modulus | Mpa | ≥30 | ||
| 11 | Vicat softening point A50 | ºC | ≥80 | ||
| 12 | Ash content | % | ≤0.1 | ||
| Product Parameters | |
| Brand Name | YUANXIAN POLYMER |
| Product Name | Dog Poop Bag |
| Material | PLA + corn starch + PBAT |
| Color | Customized |
| Size(cm) | Customized |
| Features | 1. Raw material: PLA+corn starch+PBAT, 100% Biodagradable and Compostable 2. Degradability: 3-6 months under compost condition 3. Environmentally friendly printing, highlighting personalization 4. Portable, convenient and hygienic, thickened and durable, full of toughness 5. Excellent material, firm and leak proof 6. Point break design, easy to tear 7. Paper roll core, environmental protection peer 8. Small and exquisite, multi-color options. 9. Flexible packing ways, perfect and affordable for multiple pet household |
| Our Advantage | 1. Professional ODM&OEM experience. 2. Professional equipment produces high quality products. 3. Customer success plan. 4. Experience Focusing on the R&D of plastic products. 5. Fast delivery time. 6. 100% safe payment. |
Modified Material
Film Blowing Grade YPMH-S200
Film Blowing Grade PLA Modified Material
PLA+PBAT+STARCH
Item Code: YPMH-S200
Recommended application
Shopping vest bag, wrist bag, roll bag, food preservation bag; Electronic product packaging film, household.
Appliance packaging film, medical hygiene film, etc.
Product characteristics
1) Good coloring performance, stable melt strength, and can be directly processed into various films;
2) It is usually light white or light yellow, has fragrance, is easy to be decomposed by microorganisms, and has natural antistatic property;
3) Good heat stability of raw materials, good recyclability of leftover materials, high temparature and strong shear force;
4) This product has low moisture content. It is vacuum packed and can be used after opening.
Material properties
| Item | Test method | Conditions for item | Unit | Result[1] |
| Melt flow rate | 1S0 1133 | 190ºC, 2.16kg | g/10min | 4.0-7.0 |
| Density | 1S0 1183 | 23ºC | g/cm3 | 1.27-1.32 |
| Melting point | DSC | - - |
ºC | 110-130 |
| Temperature | Typical value[2] | Reference range | |
| Melting temperature | 120ºC | 115-125ºC | |
| Temperature of film blowing heating area | Posterior segment | 025ºC | 120-130ºC |
| Middle segment | 130ºC | 125-135ºC | |
| Anterior segment | 135ºC | 130-140ºC | |
| Mould head temperature | 135ºC | 130-140ºC | |
| Upper limit of processing temperature | 180ºC | ||
| Characteristics[4] | Test method | Conditions for testing | Unit | Typical values[5] |
| Tensile strength longitudinal/transverse | 1S0 527 | 25ºC | MPa | 21/12 |
| Elongation at break longitudinal/transverse | 1S0 527 | 25ºC | % | 250/600 |
| Dart impact | 1S0 7765-1 | 25ºC | g |
150 |
| Item | Test method | Conditions for item | Unit | Result[1] |
| Melt flow rate | 1S0 1133 | 190ºC, 2.16kg | g/10min | 3.0-6.0 |
| Density | 1S0 1183 | 23ºC | g/cm3 | 1.38-1.43 |
| Melting point | DSC | - - |
ºC | 110-130 |
| Temperature | Typical value[2] | Reference range | |
| Melting temperature | 125ºC | 120-130ºC | |
| Temperature of film blowing heating area | Posterior segment | 145ºC | 140-150ºC |
| Middle segment | 145ºC | 140-150ºC | |
| Anterior segment | 150ºC | 140-150ºC | |
| Mould head temperature | 150ºC | 140-150ºC | |
| Upper limit of processing temperature | 190ºC | ||
| Characteristics[4] | Test method | Conditions for testing | Unit | Typical value[5] |
| Tensile strength longitudinal/transverse | 1S0 527 | 25ºC | MPa | 17/13 |
| Elongation at break longitudinal/transverse | 1S0 527 | 25ºC | % | 300/500 |
| Dart impact | 1S0 7765-1 | 25ºC | g |
190 |
[3]Typical films are produced by film blowing mechanism with the material YPMH-M300, film thickness is 28 microns;
[4]The data are measured by the newly produced film and can not be used as the basis for judging material quality;
[5]The above data are typical values, not guaranteed values.
1. Q: What's your main material?
Our main materials are PLA,PBS,PBAT and Corn Starch. The materials are 100% Compostable and Biodegradable, they can be degraded into H20 and C20 completely.
2. Q: What information should I let you know if I want to get a quotation?
The size of the products (Length x Width), if your bag's have the gusset, also please provide the gusset size.
We usually quote you within 24 hours after we get your inquiry. If you are in urgency to get the quotation,please call us or tell us in your mail, so that we could regard your inquiry in priority.
3. Q: The printing: How many colors printing in 1 side or 2 sides?
It will be very useful if you can provide your bag's picture. Of course, samples will be best.
4. Q: What's your MOQ?
Usually 1 tons each kind, the more the cheaper.
5. Q: What is the bag size?
You can measure the length, width and height of the goods that need to packing, we will help you calculate the required size of the bag.
We do customized products, any size & any color we can make according to your requirement.
6. Q: Can you design for me?
According to your requirement, we can add your company logo, website, phone number or your ideas on the bag....
Any color is available. Our profession designer can make design it to for you for free.
Welcome to contact with us for more details!